• Mn/Zn soft ferrite powder

Mn/Zn soft ferrite powder

Using high-purity iron oxide powder, manganese oxide powder, and zinc oxide powder as the main raw materials, various types of Mn/Zn soft ferrite powder are produced by powder metallurgy. It can supply customers to form and sinter into soft ferrite cores with required electromagnetic charatceristic.
HIMAG cooperates with CSC technical department to develop materials for different applications, such as: wide temperature low loss, high frequency low loss, high permeability, high Bs, wide temperature stable permeability and other materials; We also has the ability to customize development.

Using high-purity iron oxide powder, manganese oxide powder, and zinc oxide powder as the main raw materials, various types of Mn/Zn soft ferrite powder are produced by powder metallurgy.
It can supply customers to form and sinter into soft ferrite cores with required electromagnetic charatceristic.

HIMAG cooperates with CSC technical department to develop materials for different applications, such as: wide temperature low loss, high frequency low loss, high permeability, high Bs, wide temperature stable permeability and other materials; We also has the ability to customize development.


21.png




Product Specification Sheet


Instructions
HIMAG
Flagship Material
Characteristic
Data
Sheet
Low Loss
of
Wide Temp.
MZ95 Low core loss at 100~500 KHz and 25~100℃

 

MZ97 Low core loss at 100~500 KHz and 0~100℃  
MZ97B Low core loss at 100~500 KHz and 0~140℃  
Low Loss
at
High Frequency
MF37 Low core loss at 500~1000 KHz  
MF91S Low core loss at 800~3000 KHz  
MF93S Low core loss at 500~5000 KHz -
High
DC bias
MB92 High Bs -  Bs 25℃=600、Bs 100℃=520  
MB35 High Bs -  Bs 25℃=470、Bs 100℃=340  
MB50 High Bs -  Bs 25℃=480、Bs 100℃=345  
high-temperature stability M02 ui = 2500 @ 0~70℃  
M04A ui = 4000 @ 0~70℃  
M06A ui = 6000 @ 0~70℃  
M10B ui = 10000 @ 0~70℃ -
HIMAG all  Mn/Zn Materials